Аналіз впливу зміни параметрів лазерного випромінювання на структуроутворення при лазерному наплавленні на тонкостінну основу

Скорочена інформація про документ
dc.contributor.authorСоколовський М. В.
dc.contributor.authorСіора О. В.
dc.contributor.authorЮрченко Ю. В.
dc.contributor.authorГардер Д. А.
dc.contributor.authorБернацький А. В.
dc.contributor.authorSokolovskyi Mykola V.
dc.contributor.authorSiora Oleksandr V.
dc.contributor.authorYurchenko Yurii V.
dc.contributor.authorHarder Dmytro A.
dc.contributor.authorBernatskyi Artemii V.
dc.date.accessioned2025-05-23T06:57:34Z
dc.date.available2025-05-23T06:57:34Z
dc.date.issued2025
dc.descriptionАналіз впливу зміни параметрів лазерного випромінювання на структуроутворення при лазерному наплавленні на тонкостінну основу = Analysis of the influence of changes in laser radiation parameters on structure formation during laser cladding on a thin-walled base / М. В. Соколовський, О. В. Сіора, Ю. В. Юрченко, Д. А. Гардер, А. В. Бернацький // Зб. наук. пр. НУК. – Миколаїв : Гельветика, 2025. – № 1 (499). – С. 42–48.
dc.description.abstractПри виготовленні різних конструкцій та деталей виробів ракетно-космічної, авіаційної, хімічної, приладобудівної та інших галузей промисловості постає завдання, що полягає у наплавленні функціональних елементів, які призначені для виконання різного комплексу певних відповідальних завдань на тонкостінні деталі жорсткої конструкції таким чином, щоб запобігти проплаву тонкостінної основи під час нанесення матеріалу. Мета даної роботи – встановлення закономірностей впливу параметрів процесу лазерного наплавлення металу на структуроутворення наплавлених шарів, нанесених на тонкостінні корпусні та функціональні деталі відповідальних конструкцій. Одержані в ході виконання досліджень наукові результати планується використати при відпрацюванні технологій лазерного наплавлення виробів різних галузей промисловості. З метою вивчення даної проблеми, було проведено ряд експериментальних робіт, включаючи виготовлення серії експериментальних зразків наплавок, аналізу їх структури за допомогою оптичної мікроскопії, а також вимірювання їх мікротвердості. На базі даних, отриманих з допомогою експерименту, було проаналізовано вплив параметрів процесу лазерного наплавлення металу на структуроутворення наплавлених шарів, нанесених на тонкостінні корпусні та функціональні деталі відповідальних конструкцій. Після виконання робіт було визначено, що при лазерному наплавленні порошку високолегованої корозійностійкої сталі утворюється лита, дисперсна, характерна для багатошарового наплавлення структура наплавлених шарів, що складається із аустенітної матриці і незначних виділень вздовж границь кристалітів. При цьому було встановлено, що при наплавленні перших шарів порошкового матеріалу на тонкостінну важливим є витримування рівня погонної енергії у 45…50 Дж/мм, з подальшим збільшенням даної величини до 60 Дж/мм при висоті наплавленого елементу в 2,75–3 мм. Подальше збільшення величини погонної енергії обробки до 75 Дж/мм при наплавленні елементів більшої висоти є небажаним через збільшення зони переплаву наплавлених шарів, а також появу недоплавлених частинок металевого порошку розміром до 20 мкм.
dc.description.abstract1During manufacturing of various structures and parts of products in the aerospace, aviation, chemical, engineering and other industries, a task of cladding of functional elements intended to perform a different set of certain critical tasks on thin-walled parts with a rigid structure is required to be performed in such a way as to prevent melting of the thin-walled base during material deposition. The purpose of this study is to establish the principles of influence of the parameters of the laser cladding process of metal on the structural formation of deposited layers applied to thinwalled body and functional parts of critical structures. The scientific results obtained in the course of the research are planned to be used in the development of laser cladding technologies for products in various industries. In order to study this problem, a number of experimental works were carried out, including the manufacture of a series of experimental cladding samples, analysis of their structure using optical microscopy, and measurement of their microhardness. The data obtained from the experiment was used to analyse the influence of laser metal cladding process parameters on the structure formation of deposited layers applied to thin-walled body and functional parts of critical structures. As a result of the study, it was determined that laser cladding of high-alloy corrosion-resistant steel powder produces a cast, dispersed structure of the deposited layers characteristic to the multilayer cladding process, consisting of an austenitic matrix and minor allocations along the boundaries of crystallites. It was found that when depositing the first layers of powder material on thin-walled steel, it is important to maintain a level of heat input of 45...50 J/mm, with a further increase of this value to 60 J/mm at a height of the deposited element of 2.75–3 mm. Further increase of the processing energy up to 75 J/mm when surfacing elements of greater height is undesirable due to the increase in the remelting zone of the deposited layers, as well as the appearance of under-melted metal powder particles of up to 20 µm in size.
dc.identifier.issn2311-3405 (Print)
dc.identifier.issn2313-0415 (Online)
dc.identifier.urihttps://eir.nuos.edu.ua/handle/123456789/10530
dc.language.isouk
dc.relation.ispartofseriesУДК; 621.791.92
dc.subjectвисоколегована корозійностійка сталь
dc.subjectлазерне наплавлення
dc.subjectтонкостінні деталі
dc.subjectпорошкова металургія
dc.subjectмікротвердість
dc.subjectструктура
dc.subjecthigh-alloy corrosion-resistant steel
dc.subjectlaser cladding
dc.subjectthin-walled parts
dc.subjectpowder metallurgy
dc.subjectmicrohardness
dc.subjectstructure
dc.titleАналіз впливу зміни параметрів лазерного випромінювання на структуроутворення при лазерному наплавленні на тонкостінну основу
dc.title.alternativeAnalysis of the influence of changes in laser radiation parameters on structure formation during laser cladding on a thin-walled base
dc.typeArticle

Файли

Контейнер файлів
Зараз показуємо 1 - 1 з 1
Ескіз
Назва:
Sokolovskyi.pdf
Розмір:
772.13 KB
Формат:
Adobe Portable Document Format
Завантажити

Зібрання

№ 1 (499) 2025